Evaluation of wear resistance of dental chairside CAD/CAM glass ceramics reinforced by different crystalline phases

The mechanical properties of crystalline phase of glass ceramics are critical. This study aimed to evaluate wear resistance of different crystalline-reinforced dental chairside computer-aided design/computer-aided manufacturing (CAD/CAM) glass ceramics. Materials of feldspar (Vita Mark II, VM), leucite (IPS Empress CAD, EC), lithium disilicate (IPS e.max CAD, EX), lithium disilicate enriched with zirconia (Vita Suprinity, VS), and enamel were embedded, grounded, and polished, respectively. Samples were indented with a Vickers hardness tester to test the fracture resistance (KIC). Two-body wear tests were performed in a reciprocal ball-on-flat configuration under artificial saliva. The parameters of load force (50 N), reciprocating amplitude (500 mu m), frequency (2 Hz), and the test cycle (10,000 cycles) were selected. Specimen microstructure, indentation morphology, and wear scars were observed by scanning electron microscope (SEM), optical microscopy, and three-dimensional profile microscopy. EX, VS, and EC demonstrated significantly higher KIC values than the enamel, while ceramic materials showed smaller wear depth results. Cracks, massive delamination, and shallow plow were seen on the enamel worn scar. Long deep plow, delamination, and brittle cracks are more common for VM and EC, and short shallow plow and smooth subsurface are the characteristics of EX and VS. Greater fracture toughness values indicated higher wear resistances of the materials for the test glass ceramics. The CAD/CAM glass ceramics performed greater wear resistance than enamel. Feldspar-and leucite-reinforced glass ceramics illustrated better wear resistance similar to enamel than lithium disilicate glass ceramics, providing amicable matching with the opposite teeth.