In Situ Neutron Scattering Study Of Nanoscale Phase Evolution In Pbte-Pbs Thermoelectric Material

Introducing nanostructural second phases has proved to be an effective approach to reduce the lattice thermal conductivity and thus enhances the figure of merit for many thermoelectric materials. Studies of the formation and evolution of these second phases are essential to understanding material temperature dependent behaviors, improving thermal stabilities, as well as designing new materials. In this study, powder samples of the PbTe-PbS thermoelectric material were examined using in situ neutron diffraction and small angle neutron scattering (SANS) techniques between room temperature and elevated temperature up to 663K, to explore quantitative information on the structure, weight fraction, and size of the second phase. Neutron diffraction data showed that the as-milled powder was primarily a solid solution prior to heat treatment. During heating, a PbS second phase precipitated out of the PbTe matrix around 500K, while re-dissolution started around 600K. The second phase remained separated from the matrix upon cooling. Furthermore, SANS data indicated that there are two populations of nanostructures. The size of the smaller nanostructure increased from initially 5 nm to approximately 25nm after annealing at 650 K, while the size of the larger one remained unchanged. This study demonstrated that in situ neutron techniques are effective means to obtain quantitative information on temperature-dependent nanostructural behavior of thermoelectrics and likely other high-temperature materials. Published by AIP Publishing.