Preparation and photoluminescence properties of Tm3+-doped ZrO2 nanotube arrays

Tm3+-doped ZrO2 nanotube arrays were prepared by anodization of a Zr–Tm alloy (3 at.% Tm) obtained by a powder metallurgical method. The morphologies, structures, elemental valence, and photoluminescence properties were characterized by using scanning electron microscope, X-ray diffractometer, X-ray photoelectron spectrometer and photoluminescence analyser, respectively. Results show that preparing conditions and annealing temperatures have significant effects on the crystalline structure and photoluminescence performance. The sample TmZNT-Org prepared in formamide + glycerol organic solution is mainly monoclinic phase and the sample TmZNT-Aq prepared in aqueous solution is mainly tetragonal phase. The sample TmZNT-Org had the strongest photoluminescence peak when annealed at 800 °C, whereas both TmZNT-Aq samples annealed at 600 °C and 800 °C had the strongest photoluminescence peak. The monoclinic phase was conductive to the emission at 454 nm while the tetragonal phase was conductive to the emission at 460 nm.